Feature

●【MATERIAL】 25 Rods 1/16"x 9.84" aluminum brazing rods are included in the package. The chemical composition of the brazing rods: Si 12%, Mg≤0.10%, Fe≤0.80%, Cu≤0.03%, Zn≤0.20%, Mn≤0.15%, AL balance. Welding flux core 18%.
●【ADVANTAGES】Brazing temperature range: 716-752°F. Solidus: 716°F, Liquidus752°F. Tensile Strength ( RM): 130N/mm². The aluminum soldering rods has good fluidity during welding, strong caulking, and can flow into small spaces.
●【PACKAGING】 Cloud Fire welding rod packaging has been optimized, and it is packaged in a sealed tube, which can effectively reduce the occurrence of moisture and other events compared with other packaging. The caps at both ends can be opened for easy storage and use.
●【APPLICATION】Aluminum welding rods for propane torch is suitable for leak welding of aluminum ship bottom, fuel tank, condenser; crack repair of aluminum alloy engine block, base, gearbox, aluminum parts. Notice: It is not suitable for cast iron welding.
●【SERVICE】 When you have a problem in the process of using the welding rod, please do not hesitate to contact us immediately, we will solve all problems for you. And we look forward to getting your suggestions on the welding rod, we will continue to improve the products and serve you better.

[Φ 1 & 16 Length 16.93 ]

[Φ 1 & 13 Length 16.93 ]

Description

Introduction of aluminum welding rods

Aluminum-aluminum flux-cored welding wire ?is different from the ordinary aluminum welding wire which needs to be welded with an argon arc welding machine, and it is also different from the aluminum-silicon welding wire that needs to be combined with a flux to be welded, and it can be brazed directly by flame or induction (because it comes with a flux, so there is no need for another Add flux). The tensile and shear strength of the workpiece welded by aluminum aluminum welding wire (the joint firmness is not lower than the base material), electrical conductivity, and corrosion resistance are all good, and the quality is stable.

Product parameters

Product name: Low temperature aluminum welding wire
Material: aluminum + drug core
Weight: 30g
Welding wire size: 1/16" X 9.84"
Working temperature: 380°C-400°C (716-752°F)
Tensile strength: 130N/mm²
Shear strength: 215MPa
Packing list: welding rod*21

Why choose us？

1. The working performance is stable, the welding effect is complete and smooth, and there is no sticking slag phenomenon.

2. Low melting point, excellent corrosion resistance, high thermal conductivity and good electrical conductivity.

3. No need for soldering powder, easy to use.

Instructions for use of low temperature aluminum welding wire


Step 1 Clean and polish the physical surface	Step 2 Heat the surface of the base metal until the wire temperature reaches the working temperature of 716-752°F. Do not use flames to burn the welding wire. If the surface temperature of the substrate is sufficient, the welding wire will flow well and can penetrate the metal capillary.	Step 3 when repairing thin aluminum, first heat the aluminum base material to a suitable working temperature, and then use the welding wire to fuse it back and forth to form a weld. You can only use a metal brush to melt the wires and solder them with welds. Use propane gas to weld small objects, use industrial gas or induction heating device to heat and weld large objects, and cool down naturally after welding.